** LW9030FR 美国杜邦增强级阻燃级
详细描述
-
-
** LW9030FR 美国杜邦增强级阻燃级
-
用途级别:通用级 汽车部件 薄壁部件
-
-
Physical Nominal ValueUnitTest MethodDensity1.57g/cm³ISO 1183 Molding ShrinkageISO 294-4 Across Flow0.80%Flow0.30%Water AbsorptionISO 62 Saturation, 23°C, 2.00 mm0.72%Equilibrium, 23°C, 2.00 mm, 50% RH0.21%Mechanical Nominal ValueUnitTest MethodTensile Modulus10500MPaISO 527-2 Tensile Stress (Break)125MPaISO 527-2 Tensile Strain (Break)1.8%ISO 527-2 Tensile Creep ModulusISO 899-1 1 hr9500MPa1000 hr7400MPaFlexural Stress175MPaISO 178 Impact Nominal ValueUnitTest MethodCharpy Notched Impact StrengthISO 179/1eA -30°C8.0kJ/m²23°C8.0kJ/m²Charpy Unnotched Impact StrengthISO 179/1eU -30°C40kJ/m²23°C40kJ/m²Notched Izod Impact StrengthISO 180/1A -30°C7.0kJ/m²23°C7.0kJ/m²Unnotched Izod Impact StrengthISO 180/1U -30°C35kJ/m²23°C35kJ/m²Thermal Nominal ValueUnitTest MethodHeat Deflection Temperature0.45 MPa, Unannealed220°CISO 75-2/B 1.8 MPa, Unannealed190°CISO 75-2/A Vi** Softening Temperature150°CISO 306/B50 Melting Temperature 3225°CISO 11357-3 CLTEISO 11359-2 Flow2.5E-5cm/cm/°CTransverse8.0E-5cm/cm/°CElectrical Nominal ValueUnitTest MethodSurface Resistivity1.0E+14ohmsIEC 60093 Volume Resistivity> 1.0E+15ohms·cmIEC 60093 Electric StrengthIEC 60243-1 --28kV/mm1.00 mm 428kV/mm2.00 mm 520kV/mmRelative PermittivityIEC 60250 100 Hz3.801 MHz3.60Dissipation FactorIEC 60250 100 Hz3.0E-31 MHz0.015**parative Tracking Index400VIEC 60112 Flammability Nominal ValueUnitTest MethodFlame Rating1.50 mmV-0UL 94, IEC 60695-11-10, -20 3.00 mm5VAUL 94, IEC 60695-11-10, -20 0.750 mmV-0IEC 60695-11-10, -20 Oxygen Index27%ISO 4589-2 Burning Rate 6 (1.00 mm)DNIISO 3795 Fill Analysis Nominal ValueUnitMelt Density1.42g/cm³Specific Heat Capacity of Melt1850J/kg/°CThermal Conductivity of Melt0.26W/m/K** Nominal ValueUnitDrying Temperature120°CDrying Time2.0 to 4.0hrSuggested Max Moisture0.040%Processing (Melt) Temp240 to 260°CMelt Temperature, Optimum250°CMold Temperature30.0 to 130°CMold Temperature, Optimum80°CHolding Pressure60.0MPaBack PressureAs low as possibleDrying Re**mendedyesEjection Temperature170°CHold Pressure Time3.00s/mm -